* Cautions during brazing

1 General cautions

1) The brazing strength should be high as required.

2) After operation, airtightness should be kept under a pressurized condition.

3) During brazing do not allow component materials to become damaged due to overheating.

4) The refrigerant pipe work should not be come blocked with scale or flux.

5) The brazed part should not restrict the flow in the refrigerant circuit.

6) No corrosion should occur from the brazed part.

2 Prevention of overheating

Due to heating, the interior and exterior surfaces of treated metal may oxidize. Especially, when the interior of the

refrigerant circuit oxidizes due to overheating, scale occurs and stays in the circuit as dust, thus exerting a fatally adverse

effect. So, make brazing at adequate brazing temperature and with a minimum of heating area.

3 Overheating protection

In order to prevent components near the brazed part from overheating damage or quality deterioration due to flame or

heat, take adequate steps for protection such as (1) by shielding with a metal plate, (2) by using a wet cloth, and (3) by

means of heat absorbent.

4 Movement during brazing

Eliminate all vibration during brazing to protect brazed joints from cracking and breakage.

5 Oxidation preventive

In order to improve the brazing efficiency, various types of antioxidant are available on the market. However, the con-

stituents of these are widely varied, and some are anticipated to corrode the piping materials, or adversely affect HFC

refrigerant, lubricating oil, etc. Exercise care when using an oxidation preventive.

8.3 Installation, removal and servicing

8.3.1 Tools for R410A

In the case of an air conditioner using R410A, in order to prevent any other refrigerant from being charged accidentally, the service

port diameter of the outdoor unit control valve (3-way valve) has been changed. Also, to increase the pressure resisting strength,

flare processing dimensions and sizes of opposite sides of flare nuts (for copper pipes with nominal diameters 1/2 and 5/8) have

been changed. During installation/service, therefore, prepare tools exclusive for R410A shown in (1) on page 134 and general tools

shown in (2) on page 135.

Fig.5 Prevention of oxidation during brazing

Flow meter

Stop valve

Reducing

valve

Piping

Rubber plug for sealing

From the nitrogen cylinder

Nitrogen gas

Missbrauch melden von Frage und/oder Antwort

Libble nimmt den Missbrauch seiner Dienste sehr ernst. Wir setzen uns dafür ein, derartige Missbrauchsfälle gemäß den Gesetzen Ihres Heimatlandes zu behandeln. Wenn Sie eine Meldung übermitteln, überprüfen wir Ihre Informationen und ergreifen entsprechende Maßnahmen. Wir melden uns nur dann wieder bei Ihnen, wenn wir weitere Einzelheiten wissen müssen oder weitere Informationen für Sie haben.

Art des Missbrauchs:

Forenregeln

Um zu sinnvolle Fragen zu kommen halten Sie sich bitte an folgende Spielregeln:

Lesen Sie zuerst die Anleitung;
Schauen Sie nach, ob die Frage bereits gestellt wurde;
Stellen Sie die Frage so deutlich wie nur einigermaßen möglich;
Erwähnen Sie was Sie bereits versucht haben um das Problem zu lösen;
Ist Ihr Problem von einem Besucher gelöst dann lassen Sie ihn / sie wissen in diesem Forum;
Falls Sie reagieren möchten, so verwenden Sie bitte das Antworten- Formular;
Da ihre Frage für alle Besucher sichtbar ist, sollten Sie lieber keine persönliche Daten erwähnen.

Mitsubishi SKM25ZG-S Seite 136

Brauchen Sie Hilfe? Stellen Sie Ihre Frage.

Missbrauch melden von Frage und/oder Antwort

Art des Missbrauchs:

Forenregeln

Neu registrieren

Andere Handbücher von Mitsubishi SKM25ZG-S

Das Handbuch wird per E-Mail gesendet. Überprüfen Sie ihre E-Mail.

Ihre Frage wurde zu diesem Forum hinzugefügt

Info